DB45/T 2524-2022 高速公路沥青路面施工技术规范

ICS93.080.20

CCSP66

45

广西壮族自治区地方标准

DB45/T2524—2022

高速公路沥青路面施工技术规范

Technicalspecificationsforconstructionofexpresswayasphalt

pavements

2022-06-24发布2022-07-30实施

广西壮族自治区市场监督管理局  发布

DB45/T2524—2022

目次

前言······························································································································II

引言·····························································································································III

1范围····························································································································1

2规范性引用文件·············································································································1

3术语和定义···················································································································1

4基本规定······················································································································2

5材料····························································································································2

6热拌沥青混合料路面·····································································································10

7透层、粘层、封层········································································································23

8特殊沥青路面铺装········································································································26

9施工质量管理与检查验收·······························································································27

I

DB45/T2524—2022

前言

本文件按照GB/T1.1—2020《标准化工作导则第1部分：标准化文件的结构和起草规则》的规定

起草。

请注意本文件的某些文件可能涉及专利。本文件的发布机构不承担识别专利的责任。

本文件由广西壮族自治区交通运输厅提出并宣贯。

本文件由广西交通运输标准化技术委员会归口。

本文件起草单位：广西交科集团有限公司、广西交通投资集团有限公司、广西路桥工程集团有限公

司、广西路建工程集团有限公司、广西交科新材料科技有限责任公司。

本文件主要起草人：张洪刚、谭华、江羽习、黎水昌、彭少龙、岳爱军、张红波、谭继宗、黄新颜、

谢泽华、朱剑宏、陆宏新、张大斌、邓娟华、唐清文、熊保林、尹业豪、陈杰、熊剑平、赵承伟、任少

博、吕庆伟、刘平、王秋敏、谭伟丽。

II

DB45/T2524—2022

引言

我国行业标准《公路沥青路面施工技术规范》（JTGF40—2004）颁布实施以来，对全国公路沥青

路面施工有重要的指导作用。广西高速公路沥青路面发展起步较晚，2004年开始铺筑第一条高速公路沥

青路面以来，仅有十余年的历史。广西地处我国华南高温多雨地区，雨季与高温季节同期，对沥青路面

的高温稳定性和水稳定性提出了较为严峻的考验，编制组从第一条高速公路沥青路面开始，就特别注重

结合广西的气候特点，优选沥青路面材料，优化沥青混合料组成设计，积极采用新材料、新技术、新设

备和新工艺提高沥青路面施工质量。

本文件是在广泛调研和总结我国高速公路沥青路面施工技术经验的基础上，结合广西的气候条件和

材料特点，经过深入研究和工程验证提出的。主要技术内容有：提出了适合广西气候特点的沥青路面材

料、矿料级配、马歇尔稳定度和动稳定度试验技术要求；进一步优化高速公路沥青路面施工设备组合和

工艺参数。

III

DB45/T2524—2022

高速公路沥青路面施工技术规范

1范围

本文件界定了高速公路沥青路面施工技术涉及的术语和定义，规定了沥青路面施工准备、材料、热

拌沥青混合料路面、沥青路面功能层、特殊沥青路面铺装、施工质量管理与检查验收的要求。

本文件适用于高速公路沥青路面施工，其他等级公路、市政公路沥青路面施工可参照执行。

2规范性引用文件

下列文件中的内容通过文中的规范性引用而构成本文件必不可少的条款。其中，注日期的引用文件，

仅该日期对应的版本适用于本文件。不注日期的引用文件，其最新版本（包括所有的修改单）适用于本

文件。

JT/T533沥青路面用纤维

JTG3450公路路基路面现场测试规程

JTGE20公路工程沥青及沥青混合料试验规程

JTGE42公路工程集料试验规程

JTGF40公路沥青路面施工技术规范

DB45/T1098橡胶沥青路面施工技术规范

DBJT45/T003SBS改性沥青中改性剂掺量及分布均匀性评价技术指南

3术语和定义

下列术语和定义适用于本文件。

3.1

湖沥青trinidadlakeasphalt

湖相沉积环境中形成的天然沥青，其特点是含有一定的黏土矿物，沥青中的轻质组分经过充分氧化，

沥青质和树脂等胶质组分含量较高。

3.2

湖改性沥青modifiedtrinidadlakeasphalt

以湖沥青为主要改性剂，经高温熔化、磨细，按照一定比例与沥青充分混合制成的沥青结合料。

3.3

橡胶沥青asphaltrubber

以废胎胶粉为主要改性剂，按一定比例与沥青掺配，经过高温搅拌、剪切和发育制成的沥青结合料。

3.4

改性胶粉橡胶沥青modifiedcrumbrubberasphalt

以改性废胎胶粉为主要改性剂，按一定比例与沥青掺配，经拌和、发育，制成的沥青结合料。

3.5

胶粉复合改性沥青crumbrubbermodifiedasphalt

1

DB45/T2524—2022

废胎胶粉与一种或多种改性剂，按照一定比例与沥青掺配，经拌和、发育，制成的沥青结合料。

4基本规定

4.1沥青路面施工应建立完善的质量和安全保证体系，制定专项施工技术方案和安全方案。

4.2高速公路沥青路面施工，场站建设、机械配套和工艺过程应符合行业标准化施工的要求。

4.3应根据当地的气候分区特点，选用沥青材料和沥青混合料的技术指标，符合本文件的相应要求。

4.4应采用热拌沥青混合料工艺进行沥青路面施工，施工温度应符合本文件的相应控制要求。

4.5沥青路面施工应有足够的材料贮备和连续摊铺工作面，满足均衡、连续施工要求。

4.6沥青路面的施工环境条件应符合本文件的相应要求，不准许在雨天或有交叉污染条件下施工。

4.7沥青混合料面层与基层之间、分层铺筑的沥青面层之间应设功能层，满足层间处理和功能要求。

4.8沥青路面施工应符合节能减排和环境保护的要求，施工过程中回收粉尘及废料应妥善处理。

5材料

5.1一般规定

5.1.1沥青材料进场前应取得型式检验报告或商检报告，采购和运输过程中应进行料源控制。

5.1.2各种材料应按本文件规定的频率和试验方法进行抽检，合格后才能进场贮存和使用。

5.2道路石油沥青

5.2.1根据沥青路面交通条件、气候分区、混合料类型和层位功能，选用A级道路石油沥青,按JTGE20

的方法试验，各技术指标应符合表1的要求。

表1A级道路石油沥青技术要求

质量指标

序号项目试验方法

70号50号

1针入度(25℃,100g,5s)/0.1mm60～7050～60T0604

2针入度指数PI-1.5～＋1.0T0604

3延度(5cm/min,15℃)/cm≥10080T0605

4延度(5cm/min,10℃)/cm≥1510T0605

5软化点(环球法)/℃≥4649T0606

6闪点(TOC)/℃≥260T0611

7含蜡量(蒸馏法)/％≤2.0T0615

8密度(15℃)/(kg/m3)实测记录T0603

9溶解度(三氯乙烯)/％≥≥99.5T0607

1060℃动力粘度/(pa·s)≥180200T0620

2

DB45/T2524—2022

表1A级道路石油沥青的技术要求（续）

质量指标

序号项目试验方法

70号50号

质量损失/％≤±0.8T0610

11RTFOT后针入度比/％≥6163T0610

延度(10℃)/cm≥64T0610

注：表中PI值、10℃延度可作为选择性指标。

5.2.2沥青路面各层位及改性沥青的基质沥青宜选用A级70号沥青；当地最热月平均气温大于30℃、

最冷月平均温度大于10℃、设沥青混合料中面层时，中面层可选用A级50号沥青。

5.2.3道路石油沥青应按品种、标号分开存放，散装沥青的贮存温度宜控制在120℃～140℃，最高

温度不应超过150℃。

5.2.4长期不使用的沥青可在自然温度下贮存。

5.3乳化沥青

5.3.1乳化沥青适用于喷洒透层、粘层与封层、修补裂缝等。乳化沥青的品种和适用范围宜符合表2

的规定。

表2乳化沥青品种及适用范围

分类品种及代号适用范围

PC-1表处、下封层

PC-2透层油及基层养生用

阳离子乳化沥青

PC-3粘层油用

BC-1稀浆封层

PA-1表处、下封层

PA-2透层油及基层养生用

阴离子乳化沥青

PA-3粘层油用

BA-1稀浆封层

5.3.2乳化沥青的质量按JTGE20的方法试验，应符合表3的规定。

表3道路用乳化沥青技术要求

品种及代号

阳离子阴离子

试验项目试验方法

喷洒用拌和用喷洒用拌和用

PC-1PC-2PC-3BC-1PA-1PA-2PA-3BA-1

破乳速度快慢快或中慢或中快慢快或中慢或中T0658

粒子电荷阳离子(＋)阴离子(-)T0653

筛上残留物(1.18mm筛)/%≤0.10.1T0652

3

DB45/T2524—2022

表3道路用乳化沥青技术要求（续）

品种及代号

阳离子阴离子

试验项目试验方法

喷洒用拌和用喷洒用拌和用

PC-1PC-2PC-3BC-1PA-1PA-2PA-3BA-1

恩格拉粘度计E252～101～61～62～302～101～61～62～30T0622

粘度

道路标准粘度计C25.3/s10～258～208～2010～6010～258～208～2010～60T0621

残留分含量/%≥5050505550505055T0651

蒸发溶解度/%≥97.597.5T0607

残留物针入度(25℃)/(0.1mm)50～20050～30045～15050～20050～30045～150T0604

延度(15℃)/cm≥4040T0605

与粗集料粘附性(裹附面积)≥2/3/2/3/T0654

与粗、细粒式集料拌和试验/均匀/均匀T0659

常温贮存稳定性/%1d11

T0655

≤5d55

5.3.3乳化沥青类型根据集料品种及使用条件选择，阳离子乳化沥青可适用于各种集料品种；阴离子

乳化沥青适用于碱性石料。乳化沥青的破乳速度、粘度宜根据用途与施工方法选择。

5.3.4制备乳化沥青用的基质沥青应符合表1中A级70号沥青的技术要求。

5.3.5乳化沥青宜集中生产，存放在立式贮存罐中，并保持适当搅拌，贮存期不准许出现离析、冻结

和破乳。

5.4改性沥青

5.4.1应根据沥青路面交通条件、气候分区、混合料类型和层位功能，选用改性沥青。SBS改性沥青、

橡胶沥青、改性胶粉橡胶沥青或胶粉复合改性沥青适用于各种类型、各层位的沥青路面；湖改性沥青适

用于沥青路面中面层。

5.4.2用于生产改性沥青的基质沥青应符合表1中A级70号沥青的技术要求，与改性剂的配伍性良好。

5.4.3SBS改性沥青的选用符合下列要求：

——SBS改性剂宜选用分子量较大、弹性恢复性能良好的星型或线型改性剂，单独使用线型SBS改

性剂时掺量不宜小于5%，使用星型改性剂时掺量不宜小于4%；

——SBS改性沥青宜采用工厂化生产；现场集中生产时，所使用的原材料、SBS掺量和生产工艺应

符合标准化管理要求，经过试生产和现场抽检合格后应取得认可；

——SBS的贮存温度不应超过170℃，生产后使用时间超过48h时，宜采用较低温度贮存；

——选用SBS（Ⅰ类）改性沥青中的Ⅰ-D类型，按JTGE20的方法试验，各技术指标应符合表4的

要求；

——采用胶粉与SBS复合改性且SBS掺量大于3%时，复合改性沥青应符合表4的要求。

表4SBS（Ⅰ类）改性沥青技术要求

序号试验项目指标要求试验方法

1针入度(25℃,100g,5s)/0.1mm40～60T0604

2针入度指数PI0～2T0604

4

DB45/T2524—2022

表4SBS（Ⅰ类）改性沥青技术要求（续）

序号试验项目指标要求试验方法

3延度(5cm/min,5℃)/cm≥20T0605

4软化点(环球法)/℃≥70T0606

≥

5运动粘度(135℃)/(Pa·s)＜3T0620

6闪点(TOC)/℃≥230T0611

7溶解度(三氯乙烯)/%≥99T0607

8弹性恢复(25℃)/%≥80T0662

9密度(15℃)/（g/cm3）实测记录T0603

10贮存稳定性离析，48h软化点差/℃≤2.5T0661

11SBS改性剂的掺量/%符合合同约定的掺量要求DBJT45/T003

质量损失/%≤±1.0

12RTFOT后针入度比/%≥65T0610

延度(5℃)/cm≥15

注1：135℃运动粘度可采用JTGE20中的“沥青布氏旋转粘度试验方法（布洛克菲尔德粘度计法）”进行测定。

注2：贮存稳定性指标适用于工厂生产的成品改性沥青。现场制作的改性沥青对贮存稳定性指标可不作要求，但必

须在制作后，保持不间断的搅拌或泵送循环，以确保使用前没有沉淀或离析。

5.4.4湖改性沥青的选用符合下列要求：

——用于生产湖改性沥青的基质沥青应符合表1中A级70号沥青的要求；作为改性剂的湖沥青应

符合表5的要求；

——湖沥青应经过磨细、除去多余的矿物质，按照型式试验确定的掺配比例和加工温度，与基质沥

青充分混合；

——生产的湖改性沥青,按照JTGE20的方法试验，应符合表6的要求。

表5湖沥青的技术要求

试验项目技术要求试验方法

针入度（25℃,100g,5s）/0.1mm0～5T0604

软化点TR&B（环与球法）/℃≥90T0606

灰分/％33～38T0614

密度(25℃)/(kg/m3)1.3～1.5T0603

TFOT后残留物针入度比（25℃）/％≥50T0609

5

DB45/T2524—2022

表6湖改性沥青的技术要求

试验项目技术要求试验方法

针入度(25℃,100g,5s)/0.1mm20～40T0604

软化点/℃≥53T0606

布氏旋转粘度（135℃）/(Pa·s)≤2.0T0625

闪点/℃≥240T0611

灰分/％9～14T0614

TFOT后残留物针入度比（25℃）/％≥60T0609

5.4.5橡胶沥青、改性胶粉橡胶沥青和胶粉复合改性沥青的选用符合下列要求：

——废胎橡胶粉应符合DB45/T1098的要求；

——改性胶粉应选用符合废胎胶粉技术要求的橡胶粉进行改性；

——橡胶沥青、改性胶粉橡胶沥青应符合表7的技术要求；

——胶粉复合改性沥青宜选用废胎胶粉与SBS复合改性；

——采用胶粉与SBS复合改性且SBS掺量不大于3%时，胶粉复合改性沥青应符合表7的要求；

——橡胶沥青和胶粉复合改性沥青的生产、贮存和使用温度不准许大于200℃。

表7橡胶沥青、改性胶粉橡胶沥青、胶粉复合改性沥青的技术要求

项目质量要求试验方法

180℃旋转粘度/(Pa·s)1.5～4.0DB45/T1098

针入度（25℃，100g，5s）/0.1mm30～60T0604

软化点/℃≥65T0606

弹性恢复（25℃）/％≥75T0662

延度（5℃，1cm/min）/cm≥5T0605

贮存稳定性（48h软化点差，163℃）/℃≤5T0661

质量损失/％≤±1.0

TFOT后25℃针入度比/％≥65T0609

延度（5℃，1cm/min）/cm≥4

5.5改性乳化沥青

5.5.1改性乳化沥青宜按表8选用。

表8改性乳化沥青的品种和适用范围

品种代号适用范围

喷洒型改性乳化沥青PCR粘层、封层、桥面防水粘结层用

改性乳化沥青

拌和型改性乳化沥青BCR改性稀浆封层和微表处、修补车辙用

6

DB45/T2524—2022

5.5.2改性乳化沥青应符合表9的技术要求。

表9改性乳化沥青技术要求

品种及代号

试验项目试验方法

PCRBCR

破乳速度快裂或中裂慢裂T0658

粒子电荷阳离子(＋)阳离子(＋)T0653

筛上剩余量（1.18mm）/%，≤0.10.1T0652

恩格拉粘度E251～103～30T0622

粘度

沥青标准粘度C25，/s8～2512～60T0621

含量/%,≤5060T0651

针入度（100g，25℃,5s）/0.1mm40～12040～100T0604

蒸发

软化点/℃，≥5053T0606

残留物

延度（5℃）/cm,≥2020T0605

溶解度(三氯乙烯)/%,≥97.597.5T0607

与矿料的粘附性，裹覆面积,≥2/3/T0654

贮存1d，≤11T0655

稳定性5d，≤55T0655

5.6粗集料

5.6.1粗集料应选用坚硬、无风化的岩石加工，可选用辉绿岩、玄武岩等基性或超基性岩，中、下面

层可选用石灰岩，选用砾岩、石英砂岩等中性或酸性岩时，应采取抗剥落措施。

5.6.2粗集料应干燥、洁净、表面粗糙，按JTGE42进行试验，应符合表10的技术要求。对于含有结

晶水和易产生热分解矿物的粗集料，宜采用经拌和机烘干或200℃烘干的粗集料进行检验。

表10沥青混合料用粗集料质量技术要求

技术要求

项目试验方法

表面层其他层次

石料压碎值/％，≤2025T0316

洛杉矶磨耗损失/％，≤2830T0317

表观相对密度，≥2.62.50T0304

t/m3

吸水率/％，≤2.03.0T0304

坚固性/％，≤58T0314

混合料151