GB/T 16309-1996 纤维增强水泥及其制品术语

ICS91-100-40

014噶8

中华人民共和国国家标准

GB/T16309一1996

纤维增强水泥及其制品术语

Termsoffiberreinforcedcement

andrelatedproducts

1996一05一15发布1996一12一01实施

国家技术监督局发布

目次

1主题内容与适用范围·········……，’’··············“··················································……1

2引用标准·····································································································……1

3基本名称···································································································”…1

4基础理论········”·····························.，········“····································”·”·····……2

5组成材料·...，’’··，’’3

6生产工艺与专用设备············”··········································“··························一·6

7制品························”·……”··················”·····.·，··“·······“··········”················……10

8性能·························.，·············“·····························································……12

9检验与应用技术··············“··············““···············································“······……14

附录A中文索引(参考件)···”··。····················”······.，···························…·…’·’·二‘’‘·二‘16

附录B英文索引(参考件)···············”·····························”····“·”··········……’二’二二‘’二二‘20

中华人民共和国国家标准

纤维增强水泥及其制品术语GB/T16309一1996

Termsoffiberreinforcedcement

andrelatedproducts

1主题内容与适用范围

本标准规定了纤维增强水泥及其制品的基本名称、基础理论、组成材料、生产工艺、专用设备、制品、

性能、检验与应用技术等方面术语的定义与涵义。

本标准适用于教学、科研、设计、生产、经贸、检验、编写及翻译技术文件。

2引用标准

GB/T1.1标准化工作导则第1单元:标准的起草与表述规则第1部分:标准编写的基本规

定

GB1.6标准化工作导则术语标准编写规定

GB10112确定术语的一般原则与方法

墓本名称

3.1纤维增强水泥fiberreinforcedcement

简称纤维水泥.由均匀分散的纤维或纤维网片与水泥净浆或砂浆组成的一种复合材料.

3.1.1石棉水泥asbestos-cement

均匀分散的石棉纤维与水泥净浆组成的一种复合材料。

3.1.2玻璃纤维增强水泥glassfibercement

简称玻璃纤维水泥。用玻璃纤维作增强材料，水泥净浆或砂浆作基体组合而成的一种复合材料。

3.1.3聚乙烯醇纤维增强水泥PVAfibercement

又称维纶纤维增强水泥(Vinylonfibercement)。简称维纶纤维水泥。以维纶纤维作增强材料，水

泥净浆或砂浆作基体组合而成的一种复合材料。

3.1.4聚丙烯膜裂纤维增强水泥fibrillatedpolypropylenefilmcement

简称聚丙烯膜裂纤维水泥。以聚丙烯膜裂纤维作增强材料，水泥净浆或砂浆作基体组合而成的

一种复合材料。

3.1.5纤维素纤维增强水泥cellulosefibercement

简称纤维素纤维水泥。以纤维素纤维作增强材料，水泥净浆作基体组合而成的一种复合材料。

3.1.6碳纤维增强水泥carbonfibercement

简称碳纤维水泥。用连续的或切短的碳纤维束作增强材料，水泥浆作基体组合而成的一种复合

材料。

3.2高性能纤维增强水泥荃复合材料highperformancefibercement-basedcomposite

用纤维增强的高性能(高强度、高弹模、高耐久性以及电磁等特性)的水泥基复合材料。

3.3混合纤维增强水泥hybridfibercement

国家技米监份局1996一05一15批准1996-12-01实施

Ge/T16309一1996

简称混合纤维水泥。采用两种与两种以上纤维混合作增强材料，水泥净浆或砂浆作基体组合而成

的一种复合材料。

3.4纤维增强硅酸钙fibercalciumsilicatematerial

用纤维与硅质和钙质材料混合经蒸压处理制成的一种复合材料。

15纤维水泥制品fibercementproducts

用纤维和水泥为主要材料制成的瓦、板、管等制品的总称。

3.5.1石棉水泥制品asbestos-cementproducts

用石棉和水泥为主要材料制成的瓦、板、管等制品的总称。

15.2石棉砂质水泥制品asbestos-sandcementproducts

用石棉和砂质水泥为主要原材料，经蒸压制成的瓦、板、管等制品的总称。

3.5.3石棉维纶纤维水泥制品asbestos-vinylonfibercementproducts

用石棉、维纶纤维和水泥为主要原材料制成的瓦、板、管等制品的总称。

15.4玻璃纤维增强水泥制品glassfibercementproducts

用抗碱玻璃纤维和低碱度水泥为主要原材料制成的制品的总称，常缩写为GRC制品。

3.6混合纤维水泥制品hybridfibercementproducts

用两种或两种以上纤维和水泥为主要材料制成的瓦、板、管等制品的总称。

3}7纤维硅酸钙制品fibercalciumsilicateproducts

用纤维和硅质与钙质材料为主要材料经蒸压制成的制品。

基础理论

4.1纤维间距理论fiberspacingmechanism

推算纤维增强混凝土初裂强度的一种理论。

4.2混合定律lawofmixtures

混合物的某些性能指标等于各组分性能指标与体积率乘积之和。

4.3「卜l.'质假说centrahypothesis

用来进一步说明水泥基材料的组成、结构与性能的假声兑。

4.4界面粘结强度interfacialbondstrength

表示纤维增强的复合材料中纤维与基体界面的粘结能力。

4.5纤维长径比aspectratio

x称纤维外形比，系纤维的长度(L)与直径(d)的比值.用L/d表示。对非圆形截面的纤维，则取与

其截面面积相等的圆的直径(当量直径).

4.6纤维取向fiberorientation

纤维在纤维水泥复合材料中的排列方向。

4.6.1一维定向one-dimentionalaligned

全部纤维沿着一个方向排列。

4.6.2维定向two-dimentionalaligned

全部纤维均在平面内按规定的两个方向排列。

4.6.3二维乱向two-dimentionalrandomorientation

全部纤维均在平面内任意地排列。

4.6.4三维乱向three-dimentionalrandomorientation

全部纤维在空间内任意地排列.

4.7纤维方向有效系数orientationfactoroffiber

表示纤维在复合材料中增强效果的一种指标。

GB/T16309一1996

8纤维体积率volumepercentageoffiber

纤维复合材料中纤维体积占总体积的百分数。

9纤维平均间距averagefiberspacing

表示乱向短纤维增强混凝土中纤维几何中心之间的平均距离。可按下式计算。

__厅d

“一”V百’下下

式中:S—纤维的平均间距，

d—纤维直径;

P—纤维体积率;

B—纤维方向有效系数。

10石棉增强效率reinforcingefficiencyofasbestos

不同品种、级别的石棉增强水泥石的效果。

11吸附性adsorption

固体或液体表面对气体或溶质的吸着能力。由于物质的表面能所引起的，按这种能的性质不同可

分为物理吸附和化学吸附两类。

12脆性brittleness

材料的一种性质，与塑性相反，直到断裂前只出现很小的弹性变形而不出现塑性变形的性能。

13塑性plasticity

使固体产生变形的力，在超过该固体的屈服点后，出现能使该固体长期保持其变形后的形状或尺

寸，亦即出现非可逆性变形的性能.

14韧性toughness

材料在外力作用下，在塑性变形的过程中吸收能量的能力。

15韧性指数toughnessindex

评价纤维增强水泥复合材料韧性的指标。

16单缝断裂singlecracking

脆性材料在受拉时破坏的一种形式。

17多缝开(断)裂multiplecracking

纤维与脆性基体组成的复合材料受拉破坏的一种形式。其特征是在受拉破坏时基体多处出现裂

缝，改变了脆性材料单缝开(断)裂的突发性破坏形式.

18断裂韧度fracturetoughness

又称断裂韧性。材料阻止裂纹扩展的能力。

19假延性pseudo-ductility

纤维增强水泥复合材料在外力作用下进入塑性变形阶段后，由于多缝开裂而表现出的延性。

组成材料

基材matrix

复合材料中的连续相，这里指纤维水泥中的水泥浆或水泥砂浆。

水泥cement

加水拌和成塑性浆体，能胶结砂石等适当材料并能在空气和水中硬化的粉状水硬性胶凝材料。

.1硅酸盐水泥portlandcement

硅酸盐水泥熟料加入适量石膏.磨细制成的水泥，即国外通称的波特兰水泥。

.2普通硅酸盐水泥ordinaryportlandcement

由硅酸盐熟料、少量混合材料、适量石膏磨细制成的水泥。

CB/T16309一1996

5.1.1.3抗硫酸盐硅酸盐水泥sulphateresitingportlandcement

由硅酸盐水泥熟料，加入适量石膏磨细制成的抗硫酸盐性能良好的水泥。

5.1.1.4低碱度水泥lowpHvaluecement

在常温下水化生成的液相的pH值低于12.5(相当于氢氧化钙饱和溶液的pH值)的水泥。

5.1.1.5砂质水泥sandcement

由硅酸盐水泥熟料、石英砂和适量的石膏共同粉磨，或用硅酸盐水泥与磨细的石英砂混合而

成的一种水硬性胶凝材料。

5.1.1.6硅质材料siliceousmaterial

含二氧化硅(Si02)材料的总称。往往同时含AIz03。磨细后，特别是在蒸汽养护和蒸压养护条

件下，能与Ca(OH)3发生化学反应而生成以水化硅酸钙为主要产物的硬化体。

5.1.1.7钙质材料calcareousmaterial

含氧化钙(CaO)材料的总称。

5.1.2净浆paste

由胶凝材料与水混合而成的浆状体。

5.1.3水泥砂浆。ementmortar

由水泥、砂加水按适当比例调制而成的砂浆.

5.2增强材料reinforcement

复合材料中起增强作用的组分。

5.2.1石棉asbestos

纤维状镁、钙、钠、铁的硅酸盐矿物的总称。

5.2.1.1蛇纹石石棉chrysotileasbestos

又称温石棉。纤维状含水的镁硅酸盐，是生产石棉水泥制品的最主要的一种石棉。

5.2.1.2角P}石石棉amphiboleasbestos

各种角闪石矿物的纤维状异种的总称。用于生产石棉水泥制品的有青石棉、铁石棉等.

5.2.2玻璃纤维glassfiber

熔融玻璃经一定的成型工艺而制成的纤维状(或丝状)物。

5.2-2.1无碱玻璃纤维(E玻璃纤维)non-alkaliglassfiber(Eglassfiber)

碱金属氧化物含量很少.具有良好电绝缘性的玻璃纤维(其碱金属氧化物含量一般小于

1%)。

5.2-2.2中碱玻璃纤维medium-alkaliglassfiber

碱金属氧化物含童在12%左右的一种玻璃纤维。

5.2-2.3抗碱玻璃纤维(耐碱玻璃纤维)alkali-resistantglassfiber

用于增强硅酸盐水泥的玻璃纤维。能耐水泥水化时析出的水化物的长期侵蚀.

5.2.2.4短切玻璃纤维原纱choppedglassfiberstrand

又称短切玻璃纤维。是将连续玻璃纤维无捻粗纱，切成长度3^12mm的丝段。

5.2.2.5玻璃纤维无捻纱glassfiberroving

将若干股连续玻璃纤维原丝不经加捻直接平行并合而成的玻璃纤维。

5.2-2.6被梭玻璃纤维coatedglassfiber

表面镇盖保护膜层的玻璃纤维无捻粗纱。

5.2-2.7被覆玻璃纤维网coatedglassfibermesh

表面援盖保护膜层的玻璃纤维网片。

5.2.3合成纤维syntheticfiber

一种化学纤维。以苯、二甲苯、苯酚、乙烯、丙烯、乙炔等为基本原料，先合成高分子化合物，再用

GB/T16309一1996

不同方法制成的纤维。

5.2-3.1聚乙烯醇纤维polyvinylalcoholfiber;PVAfiber

又称维尼纶纤维(Vinylonfiber)，简称维纶。用聚乙烯醇作主要原料制成的一种化学纤维。

5.2-3.2聚丙烯膜裂纤维polypropylenefibrillatedfilmfiber

用聚丙烯作主要原料制成的一种束状化学纤维。

5.2.4纤维素纤维cellulosefiber;graphitefiber

用某些植物的杆和韧皮等经机械或化学加工制成的纤维。

5.2.5纸纤维浆fibrouspulp

俗称纸浆。是纤维与水的混合液。

5.2.6碳纤维carbonfiber

由聚丙烯晴纤维、沥青纤维或粘胶纤维等经氧化、炭化等过程制得的含碳量为90写以上的纤

维。

5-2.7钢纤维steelfiber;steelwire

由细钢丝冷拔、剪断、薄钢片切削与熔钢抽取等方法制成的金属纤维。

5.2.8耐碱矿物棉alkali-resistantmineralwool

用天然岩石、含抗碱氧化物矿渣加其它抗碱原料经混合、熔化、用喷吹法或离心法制成的一种耐

碱溶液侵蚀的矿物纤维。

5.2.9云母mica

铁、镁、钾等的层状结构铝硅酸盐水合物，具有极完全的片状解理，可沿解理剥成具有弹性的薄

片。

5.2-10钢丝网wiremesh

用网丝直径0.5'rlmm、网格尺寸5-25mm，网格形状为正方形或矩形。用作生产钢丝网石棉

水泥波瓦用的增强材料。

5.3辅助材料

5.3.1外加剂admixture

又称添加剂。为改进水泥净浆，砂浆和混凝土的某些性能而掺入其中的物质。

5.3-1.1分散剂dispersant

又称扩散剂。能促使固体粒子的絮凝团或液滴分散为细小粒子悬浮于液体中的物质。

5.3.1.2凝聚剂coagulator;congelatingagent

又称絮凝剂。一种能溶解于水中.并使水中悬浮的固体粒子凝集与聚沉的物质。

5.3.2水玻璃waterglass

又称硅酸钠或泡花碱。分子式:Na刀.nSiO=。无色、青绿色或棕色粘稠液体。

5.3.3轻集料lightweightaggregate

堆积密度小于1100kg/m，的粗集料和小于1000kg/m，的细集料。

5.3.4膨胀珍珠岩expandedpearlite

由天然酸性火山玻璃质岩石(即珍珠岩)经焙烧膨胀而制成的粒状多孔材料。

5.3.5消石灰hydratedlime;slakedlime

又称熟石灰.由生石灰加水消化而成。主要成分为氢氧化钙.

5.3.6石英砂quartzsand

又称硅砂。主要成分为二氧化硅的粒状矿物。

5.3.7硅灰石wollastonite

又名板石。化学式:Ca,(Sipq〕，三斜晶系，晶体呈板状，集合体呈片状，放射状或纤维状。

5.3.8海泡石sepiolite

CB/T16309一1996

由菱镁矿、蛇纹石、不纯的高镁蛋白石蚀变而成，具有高度吸收性的材料。其化学组成:MgA

CSii_O,,)(OH),.·6H,O,SiO,为60.8%,Mg()为27.1%,HBO为12.10a,

5.3纸浆废液papermakingwaste

用亚硫酸盐溶液蒸煮木材、芦苇、庶渣等原料制造纸浆后排出的废液。

涂料coatings:surfacecoatings

涂于物体表面形成连续性薄膜，而具有保护、装饰或其他特殊功能的材料。

颜料pigment

不溶于分散介质(如油或水)的彩色、黑色或白色的粉状物质。

5.3.12橡胶圈rubberring

用天然或合成橡胶按一定配方硫化制成的密封圈。

生产工艺与专用设备

6.1N法L艺wetprocess

采用浓度为3%^13%的石棉水泥料浆通过过滤、真空抽吸、辊压等方法制造石棉水泥制品的一

种生产工艺

6.2半干法工艺semi-dryprocess

采用浓度为50%-70%的石棉水泥料浆，通过挤压、真空一挤压或辊压等方法制造石棉水泥制品

的一种生产工艺。

6.3干法工艺dryprocess

指加占干料重量10%-14%的水，拌成混合料，通过辊压、冲压或挤出等方法制造石棉水泥制品

的一种生产工艺。

6.4抄取法Hatschekprocess

又称圆网抄取法。是湿法工艺制造石棉水泥制品的方法之一，其成型原理与圆网造纸法相似.

6.5流浆法flow-onprocess

是利用流浆机与真空脱水装置，制造纤维水泥制品的一种方法。

6.6挤出法extrusionprocess

用挤出机制造纤维水泥制品的一种方法。

6.7注浆法injectionprocess

用注浆装II将料浆注入模具内经脱水密实制造纤维水泥制品的一种方法。

6.8喷qt法sprayingprocess

是在制造玻璃纤维增强塑料喷射成型基础上加以改进和发展而成的一种制造纤维水泥制品方法.

6.9喷吸法spray-suctionprocess

利用喷射与真空抽吸脱水装置制造纤维水泥制品的一种方法。

6.10缠绕法windingprocess

用水泥浆浸渍的连续纤维缠绕于蕊模上以制造纤维水泥制品的一种方法。

6.11预拌法premixingprocess

将束状短纤维与水泥砂浆先均匀混合制成具有一定塑性的混合物再喂入模具内制成纤维水泥制

品的方法。

6.12抹浆法lay-upprocess

将连续的纤维纱、纤维毡片或网片和水泥砂浆分别铺放在模型内制造纤维水泥制品的一种方法。

6.13纤维水泥混合料fibercementmixture

纤维水泥原材料按一定配比搅拌均匀的混合料。

6.14纤维水泥配合比fibercementmixproportion

cs/T16309一1996

纤维水泥各组成材料间的重量或体积比。

钙硅比。alc-silicaratio

硅酸钙矿物或水化硅酸钙中Ca0与Si0:的摩尔比。

石棉主体纤维。onstituentfiberofasbestos

纤维长度符合成品棉等级要求的石棉纤维.是反映成品棉质量的重要指标之一。

石棉结构textureofasbestos

机选石棉产品中纤维变形的状况。

石棉结构指数textureindexofasbestos

又称石棉结构指标。测定石棉纤维在干燥状态下的松散程度。

石棉风选pneumaticconcentrationofasbestos

又称精选。利用物料在空气流中的重力和离心力不同的作用，除掉或减少石棉中的砂粒、杂物和

部分粉尘的生产工序。

石棉松解asbestosfiberization

指对石棉纤维束进行松散和分离的工序。

石棉松解度fiberizationdegreeofasbestos

指石棉纤维松散的程度。可按下式计算。

V，___，

A=-,'XlUU为

V2

式中:A—石棉松解度，%，

V,-量简内石棉沉淀体积读数，mL;

V}—石棉悬浮液的总体积，1000mL,

制浆slurrymaking

俗称打浆。按一定顺序将石棉、代用纤维、水泥加水放在打浆设备中，根据不同成型工艺的要求制

成均匀的具有一定浓度的石棉水泥料浆。

料浆浓度slurryconcentration

指具有一定流动性的而用于生产纤维水泥制品的固体原料与水的重量比。

石棉水泥悬浮液。sbestos-cementsuspension

指抄取法工艺中，石棉水泥浆加水稀释成低浓度而使石棉水泥呈现悬浮的液体。

放浆slurrydischarging

将浓度较稠的石棉水泥料浆加水稀释到规定要求，通过机械装置，由流浆槽流入抄取机的网箱的

过程。

网箱过滤filtrationonsievecylinder

抄取法制造石棉水泥制品时，抄取成型机的网箱里滤取石棉水泥悬浮液，形成石棉水泥料层(薄

层)的过程。

料层厚度thicknessofasbertos-cememtlayer

又称薄层厚度。抄取法或流浆法成型时，粘附在成型机毛布上的石棉水泥料层的厚度.

冲料rinsing

又称冲浆。抄取法制造石棉水泥制品过程中，伏辊挤出的水冲刷初料层，使料层局部剥落的现象。

回水backwater

在制造石棉水泥制品过程中，网筒过滤、清洗毛布与网简等所排出的混水。

扯坯strippingofgreensheet

俗称搬钩。抄取法或流浆法制造石棉水泥瓦、板的过程中，当缠卷在成型筒上的料坯达到要求厚

度时，用自动控制的机械方法将料坯扯下的工序。

cs/T16309一1996

合坯superpositionofgreensheet

制造石棉水泥瓦、板时，把成型好的几片料坯通过加压装置合成整体的过程。

料坯水分watercontentofgreensheet

指在制造石棉水泥制品时，经成型筒加压后的料坯所含的水分。

真空脱水vacuumdewatering

指湿法工艺生产纤维水泥制品过程中，利用真空的原理，排除料坯中部分水分的工序。

扩孔separatingpipefrommandrel

当成型石棉水泥管达到规定厚度时，使管子内壁与管芯扩开一定间隙，以便脱出管芯的工序。

拔管pipedrawing

又称脱管.将管芯从石棉水泥管坯中抽拔出来的工序。

管端湿切endcuttingofgreenpipe

制管机卷制的石棉水泥管坯脱管芯后，两端在湿切机上进行切割整齐的工序。

预养precuring

指纤维水泥制品，在正式养护前，先在一定温度和湿度环境中经历一段时间，以提高坯体正式养

护时的初始强度的工序。

6.38养护curing

为纤维水泥制品创造适当的温、湿度条件，以利其水化硬化的工序。

湿热处理hydrothermaltreatment

又称水热处理。使纤维水泥制品在较高温度的水或蒸汽中硬化。是加速制品硬化的常用养护方

法。

蒸汽养护steamcuring

简称蒸养。一般指常压燕汽养护。是加速制品硬化的一种养护方法。

压蒸养护autoclaving

又称蒸压养护。简称压蒸或蒸压。即高压蒸汽养护，是加速制品硬化的一种养护方法。

养护制度。uringschedule

指关于养护过程中的预养、升温、恒温、降温的温度、湿度、时间以及其它措施和条件的规定。

瓦模template

生产纤维水泥波瓦用的钢模板。

管芯mandrel

生产石棉水泥管专用的成型筒。

毛布felt

又称毛毯。抄取法或流浆法成型设备中的重要部件。

石棉机械储仓asbestos-mechanicalbin

储存已精选的石棉纤维，改善劳动条件的设备。

轮碾机kollergang

把块状或棒状石棉束碾压松解的设备。

开棉机asbestosdefibringmachine

在石棉风选系统中.用于除去砂石并打散石棉束的设备。

水力松解机hygdraulicdefibringmachine

用以松解石棉，并制备石棉浆的设备。

叶轮式松解机turbinedefibringmachine

利用叶轮高速旋转产生涡流来松解石棉的设备。

泵式打浆机pump-pulper

GB/T16309一1996

用以进一步松解石棉，并制备石棉水泥料浆的设备。

荷兰式打浆机Hollarnder

造纸和石棉水泥工业用于制备纸浆、松解石棉、混合石棉水泥料浆的一种设备.

6.53逆流式混浆机counter-flowmixer

利用物料反向流动，强化搅拌石棉水泥混合料的设备。

斗式储浆池bucketrabblingvat

抄取法生产石棉水泥制品过程中，储备并保证不断供浆的设备。

6.55流浆箱flow-onbox

流浆法制造石棉水泥制品的主要装置。

6.56成型筒accumulatorroll

指由筒体、扯坯装置、测厚装置等组成，用于缠卷石棉水泥料层，并对料层加压、脱水，是湿法工艺

制瓦、板机的一个重要部件。

6.57网箱vat

指由圆网筒、搅拌器等组成，是抄取法制板、瓦、管机的一个重要装置.

回料搅拌机wastedissolver

及时处理石棉水泥制品生产过程中的未硬化的边角料与废料坯，使之重新制成石棉水泥浆的设

备。

6.59抄取法制管机Mazzapipemachine

抄取法生产石棉水泥管的主机，由料浆过滤(网箱、网筒)、料层传递(毛布)、成型加压(管芯、压力

组)、真空脱水(真空箱)、液压控制、清洗、传动等系统组成。

内真空法制管机innersuctionpipemachine

又称塑法内真空制管机。半干法工艺生产石棉水泥管的主机.主要由喂料、传动、加压、真空脱水

等装置组成。

三轴式挤压制管机triaxileextruderpipemachine

半千法简易生产石棉水泥管的主机。由三根导辊(其中一根为主动辊)，管芯、传动装置、加压机

构、无端成型布和机架等组成。

62马雅尼制管机Magnanipipemachine

意大利人Magnani所创的一种湿法制造石棉水泥管设备。

马雅尼制瓦机Magnaniboardmachine

意大利Magnani所创的一种湿法制造石棉水泥瓦的设备。

抄取法制板(瓦)机Hatscheksheet(board)machine

抄取法生产石棉水泥板(瓦)的主机。

6.65流浆法制板(瓦)机flow-onsheet(board)machine

流浆法生产纤维水泥板(瓦)的主机。

6.66千法带式制板机belttypesheetmachinefordryprocess

干法连续生产石棉水泥板的主机。

6.67真空成型机vacuumformationmachine

利用真空吸盘把石棉水泥板坯成型各种规格制品，并能同时完成切割、喂模和堆垛等工序的设

备。

6.68直压成波机corrugator

又称直压成型机。将石棉水泥料坯压成波形的设备。

6.69辊式压板机rollingmachine

俗称扣压机。是加压石棉水泥板(瓦)坯，使之进一步脱水，并起合坯作用的设备。

Gs/T16309一1996

6.70波瓦切边机。uttingmachineforcorrugatedsheet

按石棉水泥湿瓦坯规格，沿瓦坯纵、横向切去多余料边的设备。

6.71波瓦堆垛机stackingmachineforcorrugatedsheet

将石棉水泥波瓦湿坯叠放成垛的设备。

6.72喂模机templatefeedingmachine

生产石棉水泥波瓦时，把钢瓦模分片送到接坯机辊道上的设备。

6.73脱模机strippingdevice

将经养护后的石棉水泥瓦从瓦模上脱离，并分别堆成垛的设备。

6.74加筋瓦接坯机greensheetreceivingmachineforreinforcedcorrugatedsheet

生产钢丝网石棉水泥波瓦时，在普通的接坯机上增加电磁自动喂网机构的设备。

6.75高压水射流切割机high-pressurewaterjetcutter

利用大于40MPa的高压水，切割纤维水泥板坯的装置。

6.76成垛液压机stackhydraulicpress

对重叠多张板坯进行加压，提高纤维水泥板坯致密度的设备。

6.77单片液压机single-piecehydraulicpress

又称快速压机。按生产线节拍，每次加压一张坯的设备。

6.78管芯装卸装11.mandrelloadinganddischargingdevice

将管芯送至制管机的卷管部位，随之将卷好的管坯(带管芯)，送入拔管机的装置。

6.79预硬传送带precuringconveyor

简称预硬带。预硬石棉水泥管坯，并起输送作用的设备。

6.80养护窑steam-curingchamber

又称养护室。石棉水泥制品蒸汽养护的设施。

6.81隧道式养护窑tunnelcuringroom

能连续进行蒸汽养护的设施。

6.82养护坑curingpit

又称“养护池“。是间歇式常压燕汽养护的一种设施。

6.83高压釜autoclave

又称压蒸釜。对纤维水泥硅酸钙、石棉砂质水泥制品等进行高压蒸汽养护的设备。

6.84烘f'机dryer

对板材表面喷涂处理前进行烘干以降低水份的装置。

6.85穿孔机puncher

在板材上冲制各种花型孔的设备。

6.86喷涂机组spraycoatingset

用于对板材表面进行装饰性处理的设备。

制品

纤维水泥管fibercementpipe

以纤维与水泥为主要原材料制成的各种非金属管的统称。

石棉水泥管。sbestos-cementpipe

用石棉和水泥为主要原材料制成的纤维水泥管。

7.1·1石棉水泥输水管asbestos-cementpressurepipeforwatertransmission

用于铺设工、农业与民用的输水管道的石棉水泥压力管。

2石棉水泥输轻油管asbestos-cementpressurepipeforlightoil

GB/T16309一1996

用于输送轻质石油制品(汽油、煤油、柴油)的石棉水泥压力管。

1.1.3石棉水泥输盐卤管asbestos-cementpressurepipeforbitterntransmission

用于输送海水、盐卤的石棉水泥压力管。

1.1_4石棉水泥输煤气管asbestos-cementpressurepipeforgastransmission

用于输送煤气的石棉水泥压力管。

1.1.5石棉水泥电缆管asbestos-cementpipeforcableconductions

用于电力系统和通讯系统铺设电缆用的石棉水泥管。

1.1.6石棉水泥落水管asbestos-cementpipeforrainwater

用作房屋建筑屋外排除雨水用的石棉水泥管。

1.1.7石棉水泥排污管asbestos-cementpipeforevacuationofsewerage

用作房屋内外的排污水用的石棉水泥管。

1.1.8石棉水泥井管asbestos-cementpipeforwellcasing

用于钻杆托盘方法打机井用的石棉水泥井壁管。

1.2混合纤维水泥管hybridfibercementpipe

用两种以土纤维和水泥为主要原材料制成的纤维水泥管。

2纤维水泥瓦fibercementcorrugatedsheet

用纤维和水泥为主要原材料制成的轻质瓦的统称。

2.1石棉水泥波瓦asbestos-cementcorrugatedsheet

以石棉和水泥为主要原材料制成的断面呈波形的板材。

2.2石棉水泥半波瓦asbestos-cementsemi-corrugatedsheet

横截面呈半波形的石棉水泥瓦。

2.3钢丝网石棉水泥波瓦wire-meshreinforcedasbestos-cementsheet

配置钢丝网的石棉水泥波瓦.

2.4石棉水泥脊瓦asbestos-cementridgesheet

用石棉水泥波瓦铺设屋面时，屋脊处所用的石棉水泥配件。

2.5彩色石棉水泥瓦(板)colouredasbestos-cementsheet(board)

带颜色的石棉水泥瓦(板)。

2.6玻璃纤维水泥波瓦glassfibercementcorrugatedsheet

以抗碱玻璃纤维和低碱度水泥砂浆为主要原料制成的断面呈波形的瓦.

3纤维水泥板fibercementboard

用纤维和水泥为主要原材料制成的板材的统称。

3.1石棉水泥平板asbestos-cementflatboard

以石棉和水泥为基本原材料制成的轻型板材的统称。

3.2石棉水泥电气绝缘板asbestos-cementelectricalinsulatingboard

又称电工用石棉水泥加压板。以石棉和水泥为基本原材料(或掺适量电绝缘性好的辅助材料)经

加工制成的电绝缘板材。

3.3石棉水泥挠性板asbestos-cementflexibleboard

经高压成型的石棉含量高的石棉水泥平板。

3.4纤维硅酸钙板fibercalciumsilicateboard

以硅质材料(如硅藻土、石英粉等)、钙质材料(如消石灰等)和石棉、纤维素纤维等为主要原料，

成型后经高压蒸养而成的一种板材。

3.5聚乙烯醇纤维水泥板PVAfibercementboard

又称维纶纤维水泥板。以维纶纤维和水泥为主要原材料制成的轻型板材。

11

Ge/T16309一1996

轻质纤维水泥板Lightweightfibercementboard

以纤维、轻集料与水泥为主要原料制成的板材.具有密度低、机械加工性好，并有一定的隔热、隔

音效果。

玻璃纤维水泥半波板glassfiberreinforcedcementsimi-corrugatedsheet;GRCsemi-corrugated

sheet

用抗碱玻璃纤维和低碱度水泥为主要原材料制成的呈半波形截面的板材。

纤维水泥复合墙板fibercementsandwichpanel

在两层纤维水泥面板中间填充一定厚度的轻质保温材料而制成的墙板.

纤维水泥建筑配件fibercementarchitecturalparts

用纤维水泥制成的房屋建筑中的装修预制件。

7.6纤维水泥管异形件fibercementpipefittings

纤维水泥低压管道上配套应用的各种水泥连接管件。

石棉水泥管接头jointforasbestos-cementpipe

石棉水泥管的连接件。

套管式柔性接头sleeveflexiblejoint

由套管和橡胶圈组成的一种用作石棉水泥平口管的柔性接头。

法兰式柔性接头flange-typeflexiblejoint

用法兰盘、套管和橡胶圈组成的一种石棉水泥管柔性接头。

玻璃纤维增强水泥温室骨架glassfiberreinforcedcementframeworkforgreenhouse

在玻璃纤维增强水泥中配置少量钥筋制成的种植蔬菜作物用的塑料暖棚的骨架.

玻璃纤维增强水泥模板glassfiberreinforcedcementpermanentformwork

用抗碱玻璃纤维和低碱度水泥为主要原材料制成的一种建筑用的模板。

8性能

8.1密度density

物体的质量和其体积的比值。

8.2相对密度specificdensity

纤维水泥试件单位体积的质量与同体积4'C水的质量之比。

8.3表观密度apparentdensity

纤维水泥材料在自然状态下单位体积的质量。

8.4密实性denseness

纤维水泥材料的致密程度。常用密实度表示。

。一V,1MR$iMffX，。。%

孔结构porestructure

纤维水泥或制品内部气孔的数量、形状、大小、分布以及连通或密闭的状况。

孔隙率voidsratio;percentageofvoids

衡址纤维水泥制品的多孔性或致密程度的一种指标。

表观孔隙率apparentporosity

纤维水泥材料开口孔的容积与纤维水泥材料总体积(包括开口孔和闭口孔的容积)的比率(%)。

饱和吸水率coefficientofwatersaturation

纤维水泥材料水饱和状态所含水分的质量与纤维水泥材料干质量的比率，以百分率(%)表示。

含水率watercontent;moisturecontent

GB/T16309一1996

纤维水泥材料孔隙中所含水分的质量占干燥的纤维水泥材料质量的百分数。

8.10吸水性waterabsorption

纤维水泥材料吸收水分的能力.

8.11保水性waterretentivity

纤维水泥材料保持水分的能力。

8.12湿胀swelling

纤维水泥材料因吸收水分产生的体积膨胀。

8.13极限强度ultimatestrength

又称强度极限。纤维水泥材料或制品在外力(压、拉、剪、弯曲等)作用下达到破坏前，截面上所能

承受的最大应力。

8.14抗压强度compressivestrength

纤维水泥材料或制品在压力作用下达到破坏前单位面积上所承受的最大应力。

8.15轴向抗拉强度axialtensilestrength

纤维水泥材料或制品在轴向拉力作用下达到破坏前单位面积上所能承受的最大应力。

8.16抗折强度modulusofrupture;bendingstrength