T/CSTM 00753-2023 金属材料 氩含量的测定 脉冲加热惰性气体熔融-质谱法

ICS77.040.30

CCSH10

团体标准

T/CSTM00753—2023

金属材料氩含量的测定

脉冲加热惰性气体熔融-质谱法

Metallicmaterials—Determinationofargoncontent—Inertgasfusionmass

spectrometricmethod

2023-08-11发布2023-11-11实施

中关村材料试验技术联盟发布

T/CSTM00753-2023

目录

目录....................................................................................................................................................................1

前言....................................................................................................................................................................2

引言....................................................................................................................................................................3

1范围...............................................................................4

2规范性引用文件.....................................................................4

3术语和定义.........................................................................4

4原理...............................................................................4

5试剂与材料.........................................................................4

6仪器与设备.........................................................................4

7取制样.............................................................................5

8测量...............................................................................5

8.1仪器准备.....................................................................5

8.2试样称量.....................................................................6

8.3空白试验.....................................................................6

8.4校准曲线建立.................................................................6

8.5样品分析.....................................................................6

9分析结果的表示.....................................................................6

10精密度............................................................................6

11试验报告..........................................................................7

附录A...............................................................................8

附录B...............................................................................9

附录C..............................................................................10

1

T/CSTM00753-2023

前言

本文件参照GB/T1.1—2020《标准化工作导则第1部分：标准化文件的结构和起草

规则》的规定起草。

请注意本文件的某些内容可能涉及专利，本文件的发布机构不承担识别这些专利的责任。

本文件由中国材料与试验标准化委员会综合标准化领域委员会(CSTM/FC99)提出。

本文件由中国材料与试验标准化委员会综合标准化领域委员会(CSTM/FC99)归口。

2

T/CSTM00753-2023

引言

金属材料中存在的氩元素通常因为制备工艺中采用了氩气保护或氩气加压而产生。氩元素含量多

少对材料和工艺可能产生影响，需要制定统一、规范的标准来准确测定金属材料中氩元素含量。

YB/T4307-2012《钢铁及合金氧、氮和氢含量的测定脉冲加热惰气熔融-飞行时间质谱法（常规

法）》中规定了脉冲加热惰性气体熔融-质谱法测定