T/CNS 77-2022 金属材料液态铅铋控氧环境中腐蚀浸泡试验方法

ICS77.040

CCSH25

团体标准

T/CNS77—2022

金属材料液态铅铋控氧环境中

腐蚀浸泡试验方法

Testmethodforimmersioncorrosioninliquidlead-bismuthenvironmentwith

controlledoxygenconcentrationformetallicmaterials

2022-12-16发布2023-04-01实施

中国核学会  发布

T/CNS77—2022

目次

前言.................................................................................III

1范围................................................................................1

2规范性引用文件......................................................................1

3术语和定义..........................................................................1

4总体要求............................................................................1

5试验仪器和设备......................................................................1

6试样制备和要求......................................................................2

7试验条件和步骤......................................................................2

8试验结果表征及数据处理..............................................................3

9试验报告............................................................................3

附录A（资料性）高温液态铅铋反应釜示意图..............................................4

附录B（资料性）电极电位、温度与溶解氧浓度的关系......................................5

参考文献...............................................................................6

I

T/CNS77—2022

前言

本文件按照GB/T1.1—2020《标准化工作导则第1部分：标准化文件的结构和起草规则》的规定

起草。

请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别这些专利的责任。

本文件由中国核学会提出。

本文件由核工业标准化研究所归口。

本文件起草单位：广东腐蚀科学与技术创新研究院、中国科学院金属研究所、中广核研究院有限公

司、中国核动力研究设计院、生态环境部核与辐射安全中心、核工业标准化研究所。

本文件主要起草人：谭季波、吴欣强、张强、韩恩厚、邓平、高军、孙海涛、郭彦辉。

III

T/CNS77—2022

金属材料液态铅铋控氧环境中

腐蚀浸泡试验方法

1范围

本文件规定了金属材料在液态铅铋控氧环境中腐蚀浸泡试验的总体要求、试验仪器和设备、试样制

备和要