T/CNS 79-2022 压水堆用燃料包壳管高温高压水中切向微动磨损试验方法

ICS77.040.01

CCSH20

团体标准

T/CNS79—2022

压水堆用燃料包壳管高温高压

水中切向微动磨损试验方法

Testmethodfortangentialfrettingwearoffuelcladding

inhightemperaturepressurizedwaterofpressurizedwaterreactor

2022-12-16发布2023-04-01实施

中国核学会发布

T/CNS79—2022

目次

前言................................................................................III

1范围...............................................................................1

2规范性引用文件.....................................................................1

3术语和定义.........................................................................1

4总体要求...........................................................................1

5试验系统和设备.....................................................................1

6试样制备和夹具加工.................................................................2

7试验条件和步骤.....................................................................3

8试验结果分析和数据处理.............................................................4

9试验报告...........................................................................4

附录A（资料性）刚凸（或弹簧）试样与试样固定块装配图.................................5

附录B（资料性）刚凸（或弹簧）试样夹具与包壳管试样夹具整体装配结构图.................6

I

T/CNS79—2022

前言

本文件按照GB/T1.1—2020《标准化工作导则第1部分：标准化文件的结构和起草规则》的规定

起草。

请注意文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。

本文件由中国核学会提出。

本文件由核工业标准化研究所归口。

本文件起草单位：广东腐蚀科学与技术创新研究院、中国科学院金属研究所，中国核动力研究设计

院、生态环境部核与辐射安全中心、核工业标准化研究所。

本文件主要起草人：韩恩厚、王俭秋、明洪亮、张志明、张玉圣、孙磊、高李霞、赖姜、孙海涛、

郭彦辉、董振邦。

III

T/CNS79—2022

压水堆用燃料包壳管高温高压水中切向微动磨损试验方法

1范围

本文件描述了压水堆用燃料包壳管在高温高压水中切向微动磨损试验系统和设备、试样制备和夹

具加工、条件和步骤、结果分析和数据处理等内容。

本文件适用于压水堆用燃料包壳管在模拟高温高压一回路水中的微动磨损试验。