DB62/T 4341-2021 SMC改性沥青路面施工技术规程

ICS93.080

CCSR18

62

甘肃省地方标准

DB62/T4341—2021

SMC改性沥青路面施工技术规程

TechnicalspecificationforconstructionofSMCmodifiedasphaltpavement

2021-06-21发布2021-07-21实施

发布

DB62/T4341—2021

目次

前言....................................................................................................................................................................III

引言....................................................................................................................................................................IV

1范围................................................................................................................................................................1

2规范性引用文件............................................................................................................................................1

3术语和定义....................................................................................................................................................1

4符号和缩略语................................................................................................................................................3

5磨耗层适用范围及对原路面技术要求........................................................................................................3

适用范围.................................................................................................................................................3

原沥青路面的技术要求.........................................................................................................................3

原水泥路面技术要求.............................................................................................................................3

其他功能性罩面技术要求.....................................................................................................................4

6原材料............................................................................................................................................................4

一般规定.................................................................................................................................................4

沥青.........................................................................................................................................................4

SMC改性剂...........................................................................................................................................5

SMC改性沥青.......................................................................................................................................5

7SMC改性沥青混合料配合比设计...............................................................................................................6

一般规定.................................................................................................................................................6

混合料类型.............................................................................................................................................6

设计方法.................................................................................................................................................7

技术要求.................................................................................................................................................8

目标配合比设计...................................................................................................................................10

生产配合比验证...................................................................................................................................12

8SMC改性沥青混合料施工工艺.................................................................................................................12

一般规定...............................................................................................................................................12

拌和.......................................................................................................................................................12

运输.......................................................................................................................................................12

摊铺.......................................................................................................................................................12

碾压.......................................................................................................................................................12

接缝.......................................................................................................................................................13

9施工质量检查与验收..................................................................................................................................13

原材料进场复验项目检验...................................................................................................................13

施工过程中的质量控制检验...............................................................................................................15

附录A（资料性）甘肃省气候自然分区....................................................................................................17

A.1一般规定..............................................................................................................................................17

A.2自然区划..............................................................................................................................................17

附录B（规范性）SMC改性沥青混合料配合比设计方法.......................................................................18

I

DB62/T4341—2021

B.1一般规定...............................................................................................................................................18

B.2确定工程设计级配范围.......................................................................................................................18

B.3材料选择与准备...................................................................................................................................19

B.4矿料级配设计.......................................................................................................................................19

B.5混合料体积技术指标检测...................................................................................................................19

B.6确定最佳油石比（或最佳沥青用量）...............................................................................................19

B.7配合比设计检验...................................................................................................................................20

B.8配合比设计报告...................................................................................................................................20

附录C（规范性）SMC改性沥青混合料拌制...........................................................................................21

C.1拌和站准备...........................................................................................................................................21

C.2SMC改性沥青制备.............................................................................................................................21

C.3SMC改性沥青混合料拌和.................................................................................................................21

附录D（资料性）条文说明........................................................................................................................23

II

DB62/T4341—2021

前言

本文件按照GB/T1.1—2020《标准化工作导则第1部分：标准化文件的结构和起草规则》的规定

起草。

本文件由甘肃省交通运输厅提出并监督实施。

本文件由甘肃省交通运输工程标准化技术委员会归口。

本文件起草单位：甘肃省公路局、甘肃省庆阳公路局、交通运输部科学研究院、甘肃畅陇公路养护

技术研究院有限公司、甘肃省酒泉公路局。

本文件主要起草人：李福林、孙志刚、彭正军、郭朝阳、吴祥海、许辉、扈进明、贾红卫、夏玺明、

赵蔚、田苗苗、刘聪、赵静卓、魏强、武旭、张军林、李栋、孔学玉、田青业、范富军、杨建文。

各单位或个人在执行本文件过程中如发现需要修改和补充之处，请随时将意见和建议反馈至甘肃

省公路局《SMC改性沥青路面施工技术规程》编制组（地址：甘肃省兰州市南滨河东路743号，邮政编

码：730030，E-mail：591196645@），以供今后修订时参考。

III

DB62/T4341—2021

引言

随着公路行业对建设低碳交通的要求不断提高，相应的对节能减排型筑路材料的使用需求也在不

断增加。SMC改性沥青路面具有施工温度低、碳排放少的技术优势，在甘肃省多个公路养护维修项目应

用。为了规范甘肃省SMC改性沥青路面混合料设计、施工和质量控制，提高SMC改性沥青路面的工程质

量，按照《关于下达2019年度第2批地方标准制修订计划》的函（甘市监〔2019〕

136号）的要求，甘肃省公路局会同有关单位，在系统总结本省SMC改性沥青路面施工技术经验的基础

上，通过广泛调查研究、征求意见、总结工程经验、吸收有关研究成果，经深入论证，编制了本规程，

为SMC改性沥青及沥青混合料的推广应用提出了指导意见。

本文件分9章，主要内容包括：范围、规范性引用文件、术语和定义、符号和缩略语、磨耗层适用

范围及对原路面技术要求、原材料、SMC改性沥青混合料配合比设计、SMC改性沥青混合料施工工艺、

施工质量检查与验收。

IV

DB62/T4341—2021

SMC改性沥青路面施工技术规程

1范围

本文件规定了甘肃省SMC改性沥青路面原材料、混合料设计、施工和质量控制技术要求。

本文件适用于甘肃省公路沥青路面的新建、改建及养护维修工程，城市道路工程可以参考使用。

2规范性引用文件

下列文件中的内容通过文中的规范性引用而构成本文件必不可少的条款。其中，注日期的引用文件，

仅该日期对应的版本适用于本文件；不注日期的引用文件，其最新版本（包括所有的修改单）适用于本

文件。

GB/T267石油产品闪点与燃点测定法(开口杯法)

GB/T2013液体石油化工产品密度测定法

GB/T10247粘度测量方法

GB15603常用化学危险品贮存通则

GB17914易燃易爆性商品储存养护技术条件

HJ/T643固体废物挥发性有机物的测定顶空气相色谱-质谱法

JTJ073.1-2001公路水泥混凝土路面养护技术规范

JTG5142-2019公路沥青路面养护技术规范

JTGD50公路沥青路面设计规范

JTGE20公路工程沥青及沥青混合料试验规程

JTGF40公路沥青路面施工技术规范

DB62/T3136-2017公路沥青路面施工技术规范

T/CHTS10007-2019SMC改性沥青路面施工技术指南

3术语和定义

下列术语和定义适用于本文件。

SMC改性剂styrenemethylcopolymeradditive

SMC改性剂是以甲基苯乙烯嵌段共聚物（简称SMC）为主要成分，并添加一定剂量的偶联剂、固化

剂，改性树脂组成的混合物。

SMC改性沥青SMCmodifiedasphalt

以道路石油沥青为原料，加入一定比例的SMC改性剂，通过搅拌的方式混溶均匀后的混合物。

SMC复合改性沥青SMCcompositemodifiedasphalt

以SBS改性沥青为原料，加入一定比例的SMC改性剂，通过搅拌的方式混溶均匀后的混合物。

磨耗层wearingcourse

在面层顶部用坚硬的细粒料和结合料铺筑的薄结构层。

1

DB62/T4341—2021

沥青混合料试件的空隙率percentairvoidsinbituminousmixtures

压实沥青混合料内矿料及沥青以外的空隙（不包括矿料自身内部已被沥青封闭的空隙）的体积占混

合料总体积的百分率，简称VV，以百分率表示。

沥青混合料试件的沥青饱和度percentvoidsinmineralaggregatethatarefilledwithasphaltin

bituminousmixtures

沥青混合料试件内沥青部分的体积占矿料部分以外的体积（VMA）百分率，简称VFA，以百分率

表示。沥青混合料内有效沥青部分（即扣除被集料吸收的沥青以外的沥青）的体积占矿料部分以外的体

积（VMA）的百分率，称为有效沥青饱和度。

马歇尔稳定度marshallstability

按规定条件采用马歇尔试验仪测定的沥青混合料所能承受的最大荷载，简称MS，以kN计。

流值flowvalue

沥青混合料在马歇尔试验时相应于最大荷载时试件的竖向变形，简称FL，以mm计。

沥青混合料试件的矿料间隙率percentvoidsinmineralaggregateinbitumi-nousmixtures

压实沥青混合料试件中矿料部分以外的体积占混合料总体积的百分率，简称VMA，以百分率表示。

沥青混合料试件的粗集料间隙率percentvoidsincoarsemineralaggregateinbituminousmixtures

沥青混合料试件内粗集料部分以外的体积占混合料试件总体积的百分率，简称VCAmix，以百分率

表示。

渗水系数waterpermeabilitycoefficient

在规定的初始水头压力下，单位时间内渗入路面规定面积的水的体积，以mL／min计。

动稳定度dynamicstability

按规定条件进行沥青混合料车辙试验时，混合料试件变形进入稳定期后，每产生1mm轮辙变形试验

轮所行走的次数，以次/mm计。

闪点flashpoint

沥青试样在规定的盛祥器内按规定的升温速度受热时所蒸发的气体以规定的方法与试焰接触，初

次发生一瞬即灭的火焰时的温度，以℃表示。盛样器对黏稠沥青是克利夫兰开口杯（简称COC），对

液体沥青是泰格开口杯(简称TOC)。

横向力系数sidewayforcecoefficient

用于行车方向成20°偏角的测定轮以一定速度行驶时，专用轮胎与潮湿路面之间的测试轮轴向摩擦

阻力与垂直荷载的比值，简称SFC，无量纲。

构造深度texturedepth

规定区域内路表面开口空隙的深度，又称宏观纹理深度。根据测试区域和计算模型的不同，主要有

TD、SMTD、MPD等简称，以mm计。

2

DB62/T4341—2021

4符号和缩略语

SMCAC——SMC改性沥青密级配混合料

SMCFC——SMC改性沥青路面磨耗层混合料

5磨耗层适用范围及对原路面技术要求

适用范围

5.1.1根据磨耗层沥青混合料最大公称粒径的不同，磨耗层厚度一般分为1.2cm～1.5cm和1.7cm～

2.0cm两种，分别适应于SMCFC-10型和SMCFC-13型沥青混合料。

5.1.2高速公路、一级公路的磨耗层层厚宜选用1.7cm～2.0cm，采用SMCFC-13型沥青混合料，以保

证其抗滑性能。

5.1.3二级及二级以下公路磨耗层层厚宜选用1.2cm～1.5cm，采用SMCFC-10型沥青混合料。

5.1.4二级及二级以上公路磨耗层的沥青胶结料宜选用SMC复合改性沥青。

原沥青路面的技术要求

5.2.1原路面必须有足够的结构强度，即原路面整体结构强度实测弯沉值不得大于设计弯沉值的130%。

原路面局部结构强度不足的，必须根据具体情况选择合适的方法进行补强，补强后的弯沉值不得大于设

计弯沉值。

5.2.2原路面的纵向和横向平整度标准差应小于2.0mm或三米直尺的最大间隙小于4mm；当原路面

平整度不满足要求时，应采用铣刨等措施，使铣刨后的路面平整度满足上述要求。

5.2.3原路面存在以下病害时，不得采用磨耗层：

——原路面路基为软弱路基、存在不均匀沉降等；

——原路面基层松散、网裂严重，失去承载力；

——原路面面层车辙深度大于40mm；

——原路面渗水系数大于300mL/min。

5.2.4原路面存在裂缝病害时：宽度小于5mm的裂缝可不进行处理；宽度为5mm～15mm的裂缝应

进行贴缝处理，贴缝带厚度2mm～2.5mm，宽度30mm～150mm；宽度大于15mm的裂缝应进行直接灌

缝或开槽后灌缝处理，灌缝深度需大于15mm。

5.2.5原路面存在车辙病害时：深度15mm以下的车辙可直接进行罩面；车辙深度15mm～30mm必

须进行铣刨处理，保证车辙病害处的最小摊铺厚度大于罩面用混合料的公称最大粒径尺寸；车辙深度大

于30mm时，应铣刨重铺。

5.2.6原路面局部破损有坑槽、松散、拥包等病害时，应进行彻底挖补。

5.2.7原路面宜整体铣刨5mm～10mm，或者铣刨深度与罩面厚度相等；铣刨后的沥青路面清扫干净

后，宜洒布改性乳化沥青粘层油，乳化沥青洒布量以0.3kg/m2～0.5kg/m2为宜。

5.2.8原路面沥青混合料类型为SMA-16或16型断级配，且平整度标准差小于2.0mm、无麻面病害

时，可省去铣刨，并减少粘层油洒布用量。

原水泥路面技术要求

5.3.1水泥路面面板必须完整，有断板、碎裂、沉陷时，必须进行挖除，并按原设计的路面结构层进

行换板处理。

5.3.2相邻板块之间必须无错台，有错台时应进行铣刨处理。

5.3.3水泥面板之间接缝需用沥青胶砂或灌封胶填充，保证水泥面板之间连续、平整、接缝内部饱满。

3

DB62/T4341—2021

5.3.4水泥路面应精铣刨8mm～10mm，以表面露出粗骨料为宜，并清理干净已经松动的颗粒；铣刨

后的水泥路面清扫干净后，须铺筑SBS改性沥青碎石封层或橡胶沥青碎石封层，SBS改性沥青洒布量

以1.2kg/m2～1.6kg/m2为宜，橡胶沥青洒布量以1.4kg/m2～1.8kg/m2为宜，碎石应为9.5mm～13.2mm的

单档粒径集料，且经过拌和站除尘预热，碎石撒铺量为9kg/m2-11kg/m2，覆盖率为60%～80%，经碾压

后碎石封层厚度不小于8mm。

其他功能性罩面技术要求

对于铺筑厚度小于25mm的超薄罩面、不小于25mm且小于40mm的薄层罩面和不小于40mm且小于

60mm的罩面类型，其适用范围及对原路面的技术要求，应符合JTG5142的相关要求。

6原材料

一般规定

6.1.1SMC改性沥青路面使用的原材料必须经检验合格后方可使用。

6.1.2沥青、粗集料、细集料、填料的技术指标应符合JTGF40及DB62/T3136的规定。

6.1.3SMC改性剂的运输、储存安全性等要求应符合现行《中华人民共和国安全生产法》、GB15603、

GB17914等国家相关安全生产管理的有关法规、标准的规定。

沥青

6.2.1沥青的选择，应根据工程所在地区的气候分区进行选择，并符合下列表1、表2的技术要求。

表1道路石油沥青技术要求

沥青标号

指标单位等级试验方法

110号90号70号

针入度(25℃,5s,100g)0.1mm--100～12080～10060～80JTFE20T0604

适用的气候分区----2-23-21-22-22-32-22-3JTGF40附录A

针入度指数PI--A-1.5～＋1.0JTFE20T0604

软化点(R&B)不小于℃A43454445JTFE20T0606

60℃动力粘度不小于Pa.sA120160140160JTFE20T0620

10℃延度不小于cmA403030202520

JTFE20T0605

15℃延度不小于cmA100

蜡含量(蒸馏法)不大于%A2.2