GB/T 17689-2026 土工合成材料 塑料土工格栅

ICS83.140.10

CCSG33

中华人民共和国国家标准

GB/T17689—2026

代替GB/T17689—2008

土工合成材料塑料土工格栅

Geosynthetics—Plasticgeogrids

2026⁃07⁃30发布2027⁃02⁃01实施

国家市场监督管理总局

国家标准化管理委员会发布

GB/T17689—2026

目次

前言··························································································································Ⅲ

1范围·······················································································································1

2规范性引用文件········································································································1

3术语和定义··············································································································1

4分类、规格、命名和标识·······························································································2

5要求·······················································································································3

6试验方法·················································································································8

7检验规则···············································································································10

8标志、包装、运输和贮存·····························································································11

附录A（资料性）塑料土工格栅的种类说明······································································12

附录B（规范性）拉伸强度的试验方法（多肋法）································································14

附录C（规范性）拉伸强度的试验方法（单肋法）································································20

附录D（规范性）2%伸长率时的割线模量的试验方法························································23

附录E（规范性）连接点剥离力的试验方法······································································27

Ⅰ

GB/T17689—2026

前言

本文件按照GB/T1.1—2020《标准化工作导则第1部分：标准化文件的结构和起草规则》的规

定起草。

本文件代替GB/T17689—2008《土工合成材料塑料土工格栅》，与GB/T17689—2008相比，除

结构调整和编辑性改动外，主要技术变化如下：

——更改了范围（见第1章，2008年版的第1章）；

——更改了抗拉强度、标称抗拉强度的术语和定义（见3.2、3.3，2008年版的3.1、3.2）；

——增加了土工格栅、伸长率、割线模量、连接点剥离力的术语和定义（见3.1、3.4~3.6）；

——删除了标称伸长率、蠕变的术语和定义（见2008年版的3.3、3.4）；

——更改了塑料土工格栅的分类、规格及命名（见第4章，2008年版的第4章）；

——更改了塑料土工格栅的外观要求（见5.1，2008年版的5.2）；

——更改了单向拉伸聚丙烯土工格栅的性能指标要求（见表3，2008年版的5.1、5.3和表1）；

——更改了单向拉伸高密度聚乙烯土工格栅的性能指标要求（见表4，2008年版的5.1、5.3和表2）；

——更改了双向拉伸聚丙烯土工格栅的性能指标要求（见表5，2008年版的5.1、5.3和表3）；

——增加了三向拉伸聚丙烯土工格栅、单向焊接聚酯土工格栅、双向焊接聚酯土工格栅、单向焊接

聚酯纤塑土工格栅、双向焊接聚酯纤塑土工格栅、单向经编聚酯土工格栅、双向经编聚酯土工

格栅、单向注塑聚丙烯拉伸带土工格栅和双向注塑聚丙烯拉伸带土工格栅的性能指标要求

（见表6~表14）；

——增加了耐酸、碱性能的要求（见5.2.3）；

——增加了试样状态调节和试验环境（见6.1）；

增加了幅宽偏差、2%伸长率时的割线模量、连接点剥离力、灰分含量、抗紫外线抗拉强度保

——

持率及耐酸、碱性能的试验方法（见6.3、6.5、6.6、6.8、6.9、6.11）；

——更改了抗拉强度、2%和5%伸长率时的拉伸强度及标称抗拉强度下的伸长率的试验方法

（见6.4，2008年版的6.5）；

——更改了出厂检验和型式检验项目（见表15，2008年版的7.1.1和7.12）；

——更改了组批和抽样方案（见7.2，2008年版的7.2和7.3）；

——增加了包装要求（见8.2）；

——更改了贮存要求（见8.4，2008年版的8.3）。

请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。

本文件由中国轻工业联合会提出。

本文件由全国塑料制品标准化技术委员会（SAC/TC48）归口。

本文件起草单位：青岛旭域土工材料股份有限公司、中石化（北京）化工研究院有限公司、山东路德

新材料股份有限公司、泸州胜扬新材料有限公司、石家庄铁道大学、马克菲尔（长沙）新型支档科技开发

有限公司、泰安现代塑料有限公司、坦萨土工合成材料（中国）有限公司、湖北力特土工材料有限公司、

浩珂科技有限公司、肥城联谊工程塑料有限公司、河北省交通规划设计研究院有限公司、南昌天高环保

科技股份有限公司、山东铁科聚合科技有限公司、山东东锴工程材料有限公司、宏诚合成材料（江苏）有

限公司、贵州隆相新材料股份有限公司、云南众驰工程材料有限公司、山东建标技术试验检测有限公

司、四川中龙环保股份有限公司、贵州中驰环保科技发展有限公司、中钢集团郑州金属制品研究院股份

有限公司、九江茂康材料科技有限公司、安徽中路工程材料有限公司、新疆睿智新材料有限公司。

Ⅲ

GB/T17689—2026

本文件主要起草人：袁绍鹏、丁金海、夏飞、梁训美、王贺、付兴、王鹏、王珏、王金忠、汪祖才、崔金声、

张涛、马斌、张波、牛立锴、张宇达、吕建松、高桐睿、李佳兴、陆梁、付智龙、张明、何洋、彭改强、武鹏、

鲁增佩、孙倩、程玮、才洪峰。

本文件及其所代替文件的历次版本发布情况为：

——1999年首次发布为GB/T17689—1999，2008年第一次修订；

——本次为第二次修订。

Ⅳ

GB/T17689—2026

土工合成材料塑料土工格栅

1范围

本文件规定了塑料土工格栅的分类、规格、命名和标识、要求、检验规则及标志、包装、运输和贮存，

描述了试验方法。

本文件适用于塑料土工格栅的生产、检验和销售。

2规范性引用文件

下列文件中的内容通过文中的规范性引用而构成本文件必不可少的条款。其中，注日期的引用文

件，仅该日期对应的版本适用于本文件；不注日期的引用文件，其最新版本（包括所有的修改单）适用于

本文件。

GB/T13021—2023聚烯烃管材和管件炭黑含量的测定煅烧和热解法

GB/T16422.3—2022塑料实验室光源暴露试验方法第3部分：荧光紫外灯

GB/T16825.1金属材料静力单轴试验机的检验与校准第1部分：拉力和（或）压力试验

机测力系统的检验与校准

GB/T17632土工布及其有关产品抗酸、碱液性能的试验方法

QB/T2854塑料土工格栅蠕变试验和评价方法

3术语和定义

下列术语和定义适用于本文件。

3.1

土工格栅geogrid

GGR

由抗拉条带形成的，呈规则网格型式的平面网状结构土工合成材料。

3.2

抗拉强度tensilestrength

在规定的试验方法和试验条件下，土工格栅试样在外力作用下出现峰值时的拉力，折算成单位宽

度的拉力。

注：抗拉强度以千牛每米（kN/m）表示。

3.3

标称抗拉强度nominaltensilestrength

相应规格产品要求的最小抗拉强度。

注：标称抗拉强度以千牛每米（kN/m）表示。

3.4

伸长率elongation

材料试样受单轴拉伸时的标距间的伸长量与原标距的比值。

注：伸长率以%表示。

1

GB/T17689—2026

3.5

割线模量tensilesecantstiffness

单位宽度的拉力与相应伸长率值之比。

注：割线模量以千牛每米（kN/m）表示。

3.6

连接点剥离力detachedforceofjunction

焊接、注塑型土工格栅条带连接点在外力作用下剥离时的最大拉力。

注：连接点剥离力以牛（N）表示。

4分类、规格、命名和标识

4.1分类

塑料土工格栅按工艺、原料、受力方向分为以下几类，见表1。各类塑料土工格栅的说明见附录A。

表1塑料土工格栅产品分类

序号分类

1单向拉伸聚丙烯土工格栅

2单向拉伸高密度聚乙烯土工格栅

3双向拉伸聚丙烯土工格栅

4三向拉伸聚丙烯土工格栅

5单向焊接聚酯土工格栅

6双向焊接聚酯土工格栅

7单向焊接聚酯纤塑土工格栅

8双向焊接聚酯纤塑土工格栅

9单向经编聚酯土工格栅

10双向经编聚酯土工格栅

11单向注塑聚丙烯拉伸带土工格栅

12双向注塑聚丙烯拉伸带土工格栅

4.2规格

三向拉伸聚丙烯土工格栅按照标称2%伸长率时的割线模量划分，其他种类的塑料土工格栅按照

标称抗拉强度划分，见表2。

表2塑料土工格栅产品规格

单位为千牛每米

序号种类规格

1单向拉伸聚丙烯土工格栅a80、120、160、200、260

2单向拉伸高密度聚乙烯土工格栅a50、80、120、160、180、200

2

GB/T17689—2026

表2塑料土工格栅产品规格（续）

单位为千牛每米

序号种类规格

3双向拉伸聚丙烯土工格栅b20⁃20、30⁃30、40⁃40、50⁃50、60⁃60

4三向拉伸聚丙烯土工格栅c130、180、220、300、350

5单向焊接聚酯土工格栅a50⁃20、80⁃20、120⁃20、160⁃20、200⁃20、300⁃20、400⁃20

6双向焊接聚酯土工格栅a30⁃30、50⁃50、80⁃80、100⁃100、120⁃120、150⁃150

7单向焊接聚酯纤塑土工格栅a100⁃5、150⁃5、200⁃5、300⁃5、400⁃5、500⁃5

8双向焊接聚酯纤塑土工格栅a50⁃50、80⁃80、100⁃100、150⁃150、200⁃200

9单向经编聚酯土工格栅a80⁃30、100⁃30、150⁃30、200⁃30、300⁃30、500⁃30、600⁃30

10双向经编聚酯土工格栅a30⁃30、50⁃50、80⁃80、100⁃100、150⁃150、200⁃200、300⁃300、400⁃400

11单向注塑聚丙烯拉伸带土工格栅a100⁃40、120⁃40、160⁃40、200⁃40

12双向注塑聚丙烯拉伸带土工格栅a80⁃80、100⁃100、120⁃120、160⁃160

a规格为纵向标称抗拉强度。

b规格的“⁃”前为纵向标称抗拉强度，“⁃”后为横向标称抗拉强度。

c规格为标称2%伸长率时的割线模量。

4.3命名和标识

命名和标识如下。

示例1：标称抗拉强度为80kN/m的单向拉伸高密度聚乙烯土工格栅，表示为GGR/PE⁃HD/US80。

示例2：标称2%伸长率时的割线模量为180kN/m的三向拉伸聚丙烯土工格栅，表示为GGR/PP/TS180。

示例3：纵向标称抗拉强度为100kN/m，横向标称抗拉强度为5kN/m的单向焊接聚酯纤塑土工格栅，表示为

GGR/FP⁃PF/UW100⁃5。

示例4：纵、横向标称抗拉强度均为80kN/m的双向经编聚酯土工格栅，表示为GGR/PET/BK80⁃80。

5要求

5.1外观

塑料土工格栅产品应无破裂，网孔大小和形状应均匀。单向焊接聚酯土工格栅、双向焊接聚酯土

工格栅、单向焊接聚酯纤塑土工格栅和双向焊接聚酯纤塑土工格栅的焊点应无剥离，单向注塑聚丙烯

拉伸带土工格栅和双向注塑聚丙烯拉伸带土工格栅的节点应无滑移。

3

GB/T17689—2026

5.2性能指标

5.2.1基本性能

塑料土工格栅性能指标应符合表3~表14的规定。其他规格的性能指标由供需双方商定。

表3单向拉伸聚丙烯土工格栅的基本性能

规格

项目单位

80120160200260

幅宽偏差%≥-0.5

纵向抗拉强度kN/m≥80.0≥120.0≥160.0≥200.0≥260.0

纵向2%伸长率时的拉伸强度kN/m≥28.0≥42.0≥56.0≥70.0≥91.0

纵向5%伸长率时的拉伸强度kN/m≥56.0≥84.0≥112.0≥140.0≥182.0

纵向标称抗拉强度下的伸长率%≤10.0

炭黑含量%≥2.0

灰分含量%≤1.0

抗紫外线抗拉强度保持率%≥90.0

表4单向拉伸高密度聚乙烯土工格栅的基本性能

规格

项目单位

5080120160180200

幅宽偏差%≥-0.5

纵向抗拉强度kN/m≥50.0≥80.0≥120.0≥160.0≥180.0≥200.0

纵向2%伸长率时的拉伸强度kN/m≥12.0≥21.0≥33.0≥47.0≥52.0≥57.0

纵向5%伸长率时的拉伸强度kN/m≥23.0≥40.0≥65.0≥93.0≥103.0≥113.0

纵向标称抗拉强度下的伸长率%≤11.5

炭黑含量%≥2.0

灰分含量%≤1.0

抗紫外线抗拉强度保持率%≥90.0

表5双向拉伸聚丙烯土工格栅的基本性能

规格

项目单位

20⁃2030⁃3040⁃4050⁃5060⁃60

幅宽偏差%≥-0.5

纵、横向抗拉强度kN/m≥20.0≥30.0≥40.0≥50.0≥60.0

纵、横向2%伸长率时的拉伸强度kN/m≥7.0≥10.5≥14.0≥17.5≥21.0

纵、横向5%伸长率时的拉伸强度kN/m≥14.0≥21.0≥28.0≥35.0≥42.0

4

GB/T17689—2026

表5双向拉伸聚丙烯土工格栅的基本性能（续）

规格

项目单位

20⁃2030⁃3040⁃4050⁃5060⁃60

纵向标称抗拉强度下的伸长率%≤15.0

横向标称抗拉强度下的伸长率%≤13.0

炭黑含量%≥2.0

灰分含量%≤1.0

抗紫外线抗拉强度保持率%≥90.0

表6三向拉伸聚丙烯土工格栅的基本性能

规格

项目单位

130180220300350

幅宽偏差%≥-0.5

0°、30°、60°、90°方向上的2%

kN/m≥130≥180≥220≥300≥350

伸长率时的割线模量

炭黑含量%≥2.0

灰分含量%≤1.0

抗紫外线抗拉强度保持率%≥90.0

表7单向焊接聚酯土工格栅的基本性能

规格

项目单位

50⁃2080⁃20120⁃20160⁃20200⁃20300⁃20400⁃20

幅宽偏差%≥-0.5

纵向抗拉强度kN/m≥50.0≥80.0≥120.0≥160.0≥200.0≥300.0≥400.0

横向抗拉强度kN/m≥20.0≥20.0≥20.0≥20.0≥20.0≥20.0≥20.0

纵向2%伸长率时的拉伸强度kN/m≥21.0≥36.0≥48.0≥68.0≥70.0≥105.0≥140.0

纵向5%伸长率时的拉伸强度kN/m≥39.0≥64.0≥84.0≥118.0≥140.0≥210.0≥280.0

纵向标称抗拉强度下的伸长率%≤8.0

连接点剥离力N≥100

抗紫外线抗拉强度保持率%≥80.0

表8双向焊接聚酯土工格栅的基本性能

规格

项目单位

30⁃3050⁃5080⁃80100⁃100120⁃120150⁃150

幅宽偏差%≥-0.5

纵、横向抗拉强度kN/m≥30.0≥50.0≥80.0≥100.0≥120.0≥150.0

5

GB/T17689—2026

表8双向焊接聚酯土工格栅的基本性能（续）

规格

项目单位

30⁃3050⁃5080⁃80100⁃100120⁃120150⁃150

纵、横向2%伸长率时的拉伸强度kN/m≥12.0≥21.0≥36.0≥42.0≥48.0≥60.0

纵、横向5%伸长率时的拉伸强度kN/m≥22.0≥39.0≥64.0≥78.0≥84.0≥105.0

纵、横向标称抗拉强度下的伸长率%≤8.0

连接点剥离力N≥100

抗紫外线抗拉强度保持率%≥80.0

表9单向焊接聚酯纤塑土工格栅的基本性能

规格

项目单位

100⁃5150⁃5200⁃5300⁃5400⁃5500⁃5

幅宽偏差%≥-0.5

纵向抗拉强度kN/m≥100.0≥150.0≥200.0≥300.0≥400.0≥500.0

横向抗拉强度kN/m≥5.0≥5.0≥5.0≥5.0≥5.0≥5.0

纵向2%伸长率时的拉伸强度kN/m≥23.0≥34.0≥46.0≥69.0≥92.0≥115.0

纵向5%伸长率时的拉伸强度kN/m≥55.0≥82.0≥110.0≥165.0≥220.0≥275.0

纵向标称抗拉强度下的伸长率%≤9.5

连接点剥离力N